Quickly on site when a South African zinc mine experienced a premature detonation in one of its blastholes, BME investigated the incident and swiftly applied a safe strategy to proceed
According to BME technical services manager Deon Pieterse, the cause of the detonation was the reactive ground being drilled for blasting – an example of the exothermic chemical reaction that can occur between sulphide-bearing rock and ammonium nitrate-based explosives in the blasthole.
“The mine was found to have geologically bounded reactive zones within its rich zinc deposits,” commented Pieterse. “Due to the natural process of weathering and leaching, the upper benches of the transition zone are more prone to reactivity – as these benches contain more exposed sulphide or sulphide bearing rock and soils.
“In this case, an unexpected detonation of three holes occurred after the loading process was completed and before blast firing. There were no injuries associated with these events.”
The blast block was immediately evacuated and barricaded. For two days, other blast holes showed signs of reaction. This included the emission of smoke and yellow orange reacted emulsion froth coming out of the blast holes. After signs of reaction ceased, and the pit was declared safe, and an in-pit inspection was conducted. Ground samples were collected from the reactive areas and sent for ammonium nitrate and ground reactivity analysis.
Ground samples were collected from the reactive areas and sent for testing at the BME’s Losberg laboratory. Here, extreme reactions were observed in two samples of reactive ground that had been loaded with uninhibited bulk ammonium nitrate explosives.
“We monitored the temperature of the samples during testing with a temperature data logger, and measured temperatures exceeding 700°C within an hour of mixing the samples,” he said.
BME was then able to apply its urea-inhibited bulk emulsion – brand named INNOVEX RG – which is specially designed for use in reactive ground. Applying the same tests, this inhibited emulsion did not react, or cause any temperature spike.
“We then conducted ongoing characterisation work to understand the reactive ground at the mine,” said Pieterse. “As mining progresses, drill samples are analysed and tested, helping us to build reactive zone maps of the geology.”
In terms of safety practice associated with reactive ground, he explained that mines should conduct a risk assessment where they suspect reactive ground. This should include the monitoring of potential reactive ground indicators. If reactive ground is identified, he outlined a range of controls to manage this risk.
“Mines can use urea-inhibited bulk emulsion, as urea reduces the rate of reaction and slows heat build-up,” he said. “Blocks should then be kept small enough to be fully charged and fired the same day.”
He noted that, in some instances, holes may need to be sleeved with plastic liners before charging – to isolate the explosives from the blasthole walls. Drill assistants should then keep drill cuttings clear of the blast hole collars, to a radius of at least half a metre.
As a rule, personnel on the block must be kept to a minimum during the priming and stemming activities. They should also be careful to check that all explosive and initiation products used to blast reactive ground are compatible; also, each product must be qualified to operate within the temperature range.
“It is important that imported stemming material must be tested to be free of reactive ground,” he said. “Unless stemming can be done rapidly using a stemming truck, blast holes should remain unstemmed.”
He warned, however, that with no stemming in the blast holes, there may be increased air blast and more flyrock from the surface cratering.
“If the holes need to be stemmed, then this must be done just before blasting time – so that all holes remain open for long as possible to release heat,” he said. “This reduces the risk of hole deflagration and unexpected detonation.”
He highlighted another benefit of having unstemmed holes: they can be observed more easily. For instance, reacting holes may emit visible fumes, in colours of yellow, orange, red and brown. If this occurs, then the blast area should be immediately evacuated and secured, and personnel moved to a safe distance.